Austenite size

1Cr17Mn6Ni5N section nickel steel, replace grade 1Cr17Ni7, cold worked magnetic.For railway vehicles.

1Cr18Mn8Ni5N section nickel steel, replace grade 1Cr18Ni9

1Cr17Ni7 stainless steel tubes are cold worked for high strength.Railway vehicles, conveyor belts, bolts and nuts

1Cr18Ni9 has high strength after cold working, but the elongation is slightly worse than 1Cr17Ni7.Decorative parts for building.

Y1Cr18Ni9 improves cutting and ablative resistance.Most suitable for automatic lathes.Bolt and nut

Y1Cr18Ni9Se improves cutting and ablative resistance.Most suitable for automatic lathes.Rivets and screws

0Cr19Ni9 stainless steel tube as stainless heat resistant steel is the most widely used in food equipment, general chemical equipment, atomic energy industry

00Cr19Ni11 stainless steel tube than 0Cr19Ni9 lower carbon content of steel, intergranular corrosion resistance is superior, for welding without heat treatment parts

0Cr19Ni9N Add N to grade 0Cr19Ni9, the strength increases, the plasticity does not decrease.The thickness of the material is reduced.As a structural strength component

0Cr19Ni10NbN stainless steel tube in the brand 0Cr19Ni9 plus N and Nb, with the same characteristics and use of 0Cr19Ni9N stainless steel stair handrail

00Cr18Ni10N stainless steel tube in the brand 00Cr19Ni11 plus N, with the same characteristics of the above brand, use and 0Cr19Ni9N the same, but better resistance to intergranular corrosion

Work hardening of 1Cr18Ni12 compared with 0Cr19Ni9.Spinning processing, special pull, cold heading

0Cr23Ni13 stainless steel pipe corrosion resistance, heat resistance are better than 0Cr19Ni9

0Cr25Ni20 stainless steel pipe oxidation is better than 0Cr23Ni13.In fact, it is mostly used as heat resistant steel

0Cr17Ni12Mo2 stainless steel pipe in seawater and other media, corrosion resistance is better than 0Cr19Ni9.Mainly used as pitting corrosion resistant material

0Cr18Ni12Mo2Ti stainless steel tube is used for anti-sulfuric acid, phosphoric acid, formic acid, acetic acid equipment, has good resistance to intergranular corrosion

00Cr17Ni14Mo2 stainless steel tube is 0Cr17Ni12Mo2 stainless steel tube of ultra-low carbon steel, better intergranular corrosion resistance than 0Cr17Ni12Mo2

0Cr17Ni12Mo2N stainless steel tube in the brand of 0Cr17Ni12Mo2 to add N, improve the strength, do not reduce plasticity, so that the thickness of the material thin.For good corrosion resistance and high strength components

00Cr17Ni13Mo2N stainless steel pipe in the brand 00Cr17Ni14Mo2 to add N, with the same characteristics of the above brand, use and 0Cr17Ni12Mo2 the same, but better crystal corrosion resistance